Sintered SmCo
| Br [mT] | Hcb [kA/m] | Hcj [kA/m] | (B * H)max [kJ/m³] | rev. temp. –coeff [%/K] | Density [g/cm³] | max. operating temp. [°C] | |
| XG 16 | 810 – 850 | 620 – 660 | 1194 – 1830 | 110 – 127 | -0,04 | 8,3 | 250 |
| XG 18 | 850 – 900 | 680 – 700 | 1194 – 1830 | 127 – 143 | -0,04 | 8,3 | 250 |
| XG 20 | 900 – 940 | 678 – 725 | 1194 – 1830 | 150 – 167 | -0,04 | 8,3 | 250 |
| XG 22 | 920 – 960 | 710 – 748 | 1194 – 1830 | 160 – 175 | -0,04 | 8,3 | 250 |
| XG 24 | 960 – 1000 | 730 – 770 | 1194 – 1830 | 175 – 180 | -0,04 | 8,3 | 250 |
| XGS 24M | 920 – 1040 | 318 – 788 | 398 – 1194 | 175 – 199 | -0,03 | 8,4 | 350 |
| XGS 24 | 920 – 1040 | 661 – 796 | 1194 – 1990 | 175 – 199 | -0,03 | 8,4 | 350 |
| XGS 24H | 920 – 1040 | 661 – 804 | >1990 | 175 – 199 | -0,03 | 8,4 | 350 |
| XGS 26M | 1000 – 1060 | 318 – 796 | 398 – 1194 | 191 – 215 | -0,03 | 8,4 | 350 |
| XGS 26 | 1000 – 1060 | 677 – 820 | 1194 – 1990 | 191 – 215 | -0,03 | 8,4 | 350 |
| XGS 26H | 1000 – 1060 | 677 – 820 | >1990 | 191 – 215 | -0,03 | 8,4 | 350 |
| XGS 28M | 1040 – 1100 | 318 – 804 | 398 – 1194 | 207 – 231 | -0,03 | 8,4 | 350 |
| XGS 28 | 1040 – 1100 | 677 – 820 | 1194 – 1990 | 207 – 231 | -0,03 | 8,4 | 350 |
| XGS 28H | 1040 – 1100 | 677 – 820 | >1990 | 207 – 231 | -0,03 | 8,4 | 350 |
| XGS 30M | 1070 – 1120 | 318 – 804 | 398-1194 | 223 – 247 | -0,03 | 8,4 | 350 |
| XGS 30 | 1070 – 1120 | 700 – 828 | 1194-1990 | 223 – 247 | -0,03 | 8,4 | 350 |
| XGS 30H | 1070 – 1120 | 700 – 828 | >1990 | 233 – 247 | -0,03 | 8,4 | 350 |
| XGS 32M | 1090 – 1150 | 318 – 804 | 398-955 | 231 – 255 | -0,03 | 8,4 | 350 |
| XGS 32 | 1090 – 1150 | 716 – 836 | >955 | 238 – 255 | -0,03 | 8,4 | 350 |
| XGS 22LT | 930 – 1000 | 677 – 756 | >1194 | 159 – 191 | -0,01 | 8,4 | 350 |
| XGS 24LT | 960 – 1040 | 677 – 756 | >1194 | 175 – 207 | -0,01 | 8,4 | 350 |
| XGS 26LT | 1000 – 1070 | 677 – 812 | >1433 | 191 – 223 | -0,02 | 8,4 | 350 |